PVC-M給水管材
當(dāng)前位置：首頁 > 產(chǎn)品中心 > PVC-M給水管材 >
PVC-M給水管材
產(chǎn)品介紹
| 公稱壓力等級和規(guī)格尺寸 | ||||||
| 公稱外徑dn | S25 | S20 | S16 | S12.5 | S10 | S8 |
| SDR51 | SDR41 | SDR33 | SDR26 | SDR21 | SDR17 | |
| PN0.63 | PN0.8 | PN1.0 | PN1.25 | PN1.6 | PN2.0 | |
| 公稱壁厚en | ||||||
| 20 | 2.0 | 2.0 | ||||
| 25 | 2.0 | 2.0 | ||||
| 32 | 2.0 | 2.0 | ||||
| 40 | 2.0 | 2.4 | ||||
| 50 | 2.0 | 2.4 | 3.0 | |||
| 63 | 2.0 | 2.5 | 3.0 | 3.8 | ||
| 75 | 2.0 | 2.3 | 2.9 | 3.6 | 4.5 | |
| 90 | 2.0 | 2.2 | 2.8 | 3.5 | 4.3 | 5.4 |
| 110 | 2.2 | 2.7 | 3.4 | 4.2 | 5.3 | 6.6 |
| 125 | 2.5 | 3.1 | 3.9 | 4.8 | 6.0 | 7.4 |
| 140 | 2.8 | 3.5 | 4.3 | 5.4 | 6.7 | 8.3 |
| 160 | 3.2 | 4.0 | 4.9 | 6.2 | 7.7 | 9.5 |
| 180 | 3.6 | 4.4 | 5.5 | 6.9 | 8.6 | 10.7 |
| 200 | 3.9 | 4.9 | 6.2 | 7.7 | 9.6 | 11.9 |
| 225 | 4.4 | 5.5 | 6.9 | 8.6 | 10.8 | 13.4 |
| 250 | 4.9 | 6.2 | 7.7 | 9.6 | 11.9 | 14.8 |
| 280 | 5.5 | 6.9 | 8.6 | 10.7 | 13.4 | 16.6 |
| 315 | 6.2 | 7.7 | 9.7 | 12.1 | 15.0 | 18.7 |
| 355 | 7.0 | 8.7 | 10.9 | 13.6 | 16.9 | 21.1 |
| 400 | 7.9 | 9.8 | 12.3 | 15.3 | 19.1 | 23.7 |
| 450 | 8.8 | 11.0 | 13.8 | 17.2 | 21.5 | 26.7 |
| 500 | 9.8 | 12.3 | 15.3 | 19.1 | 23.9 | 29.7 |
| 560 | 11.0 | 13.7 | 17.2 | 21.4 | 26.7 | 33.2 |
| 630 | 12.3 | 15.4 | 19.3 | 24.1 | 30.0 | 37.4 |
| 710 | 13.9 | 17.4 | 21.8 | 27.2 | 33.9 | 42.1 |
| 800 | 15.7 | 19.6 | 24.5 | 30.6 | 38.1 | 47.4 |
| 管材物理力學(xué)性能 | |||
| 項目 | 單位 | 技術(shù)指標 | 試驗方法 |
| 密度 | kg/m³ | 1350-1460 | GB/T 1033-1986方法A |
| 維卡軟化溫度 | ℃ | ≥80 | GB/T 8802 |
| 縱向回縮率 | % | ≤5 | GB/T 6671-2001 |
| 二氯甲烷浸漬試驗 | 15℃，30min | 表面變化不劣于4N | GB/T 13526 |
| 落錘沖擊試驗（0℃） | TIR/（%） | ≤5 | GB/T 14152 |
| 高速沖擊試驗（22℃） | 不發(fā)生脆性破壞 | CJ/T 272.7.1.10 | |
| 液壓試驗 | 無破裂，無滲漏 | GB/T 6111-2003 | |
| 切口管材液壓試驗 | 無破裂，無滲漏 | CJ/T 272.7.1.12 | |
| C-環(huán)韌度試驗 | 韌性破壞 | CJ/T 272.7.1.13 | |
| 長期靜液壓試驗 | Mpa | σLPL≥24.5 | CJ/T 272.7.1.14 |